NON-UPSET TUBING

TECHNICAL DATA


            MAKE-UP TORQUE
FT/LBS		          
           

P-110

  

13CR-110

          
  SIZE   WT/FT WALL DRIFT TUBE
I.D.		 PITCH MIN. OPT. MAX.   MIN. OPT. MAX. TENSILE
YIELD
(LBS)		 INTERNAL
PRESSURE
(PSI)		 COLLAPSE
PRESSURE
(PSI)		 COUPLING
O.D.
±  1%		 STRING
LENGTH
S.F.=1.6
2 3/8" 4.00 .167 1.947 2.041 10 840 1120 1400   825 1100 1375 82,860 13,530 12,740 2.875 12,946
2 3/8" 4.60 .190 1.901 1.995 10 1005 1340 1675   985 1315 1645 98,900 15,400 16,130 2.875 13,437
2 3/8" 5.80 .254 1.773 1.867 10 1440 1920 2395   1410 1880 2355 141,600 20,580 21,010 2.875 15,258
2 3/8" 6.60 .295 1.691 1.785 10 1700 2265 2835   1670 2225 2785 167,480 22,070 23,930 2.875 15,859
2 3/8" 7.35 .336 1.609 1.703 10 1950 2600 3250   1915 2555 3195 192,190 22,070 26,720 2.875 16,342
2 7/8" 6.40 .217 2.347 2.441 10 1450 1935 2415   1425 1900 2375 145,150 14,530 14,550 3.500 14,174
2 7/8" 7.80 .276 2.229 2.323 10 1935 2580 3225   1900 2535 3170 193,710 18,480 19,090 3.500 15,521
2 7/8" 8.60 .308 2.165 2.259 10 2190 2920 3650   2150 2870 3585 219,050 20,620 21,040 3.500 15,919
2 7/8" 9.35 .340 2.101 2.195 10 2435 3250 4060   2395 3190 3990 243,670 22,760 22,940 3.500 16,288
2 7/8" 10.50 .392 1.997 2.091 10 2820 3760 4700   2770 3695 4620 282,190 22,910 25,900 3.500 16,797
2 7/8" 11.50 .440 1.901 1.995 10 3160 4210 5265   3105 4140 5175 316,070 22,910 28,510 3.500 17,177
3 1/2" 7.70 .216 2.943 3.068 10 1680 2240 2800   1655 2205 2760 178,950 11,880 9,730 4.250 14,525
3 1/2" 9.20 .254 2.867 2.992 10 2055 2740 3425   2025 2695 3370 218,740 13,970 13,530 4.250 14,860
3 1/2" 10.20 .289 2.797 2.922 10 2390 3190 3985   2355 3140 3920 254,500 15,890 16,660 4.250 15,594
3 1/2" 12.70 .375 2.625 2.750 10 3185 4245 5305   3135 4175 5220 338,790 20,620 21,040 4.250 16,672
4" 9.50 .226 3.423 3.548 8 1735 2310 2885   1710 2275 2845 198,010 10,870 7,900 4.750 13,026
4" 13.20 .330 3.215 3.340 8 2815 3755 4695   2775 3700 4620 321,790 15,880 16,650 4.750 15,236
4 1/2" 12.60 .271 3.833 3.958 8 2435 3245 4055   2400 3200 4000 287,000 11,590 9,210 5.200 14,236
4 1/2" 15.20 .337 3.701 3.826 8 3190 4250 5310   3140 4190 5235 375,770 14,410 14,340 5.200 15,451
4 1/2" 17.00 .380 3.615 3.740 8 3665 4885 6105   3610 4815 6015 431,980 16,250 17,000 5.200 15,881


NOTES: Per API 5C1:
Sect. 5.2.4
Joints should be made up approximately 2 turns beyond the hand-tight position.
For basic power-tight make-up, the face of the coupling or box advances to the vanish point. (API 5B Fig. 8)
Make-up target should be governed by position rather than torque. (API 5C1 Table 3)

Sect. 5.3.1
1. These values apply to tubing with Zinc-plated or Phosphate-coated couplings, utilizing API Mod Thread Compound.
    Thread compounds other than API Mod, may require different torque values, due to different frictional properties. (API 5C1 Sect. 4.3.4)
2. Connections with Tin-plated couplings can be made up at 80% of the listed torque values.
3. Round thread connections with PTFE seal rings should be made up at 70% of the listed torque value.


Reproduced courtesy of the American Petroleum Institute

This data was compiled from the following API documents:
API Spec. 5CT Fifth Ed. Apr. 1, 1995
API RP 5C1 Seventeenth Ed. Nov. 1, 1994
API Bull. 5C2 Twentieth Ed. May 13, 1987
API Bull. 5C3 Sixth Ed. Oct. 1, 1994
API Spec 5B Fifteenth Ed. Oct. 1, 2008

This technical data is for general information only.   Although every effort has been made to ensure accuracy, Benoit makes no warranty for any loss or damages due to its use.